CARBIDE
Drill Stock Dimensions (mm)
Dia. L1 L3 L9 D4
D1 Hole Depth
(mm) (l/d) DP1021
Type
Order Number
3 r MPS1-1900S-DIN 131 79 50 20 4
a -1900S-DIN-C 131 79 50 20 2
19.0 3 r -1900L-DIN 153 101 50 20 4
5 a -1900L-DIN-C 153 101 50 20 2
5 4
2
3 r -1950S-DIN 131 79 50 20 4
a -1950S-DIN-C 131 79 50 20 2
19.5 3 r -1950L-DIN 153 101 50 20
5 a -1950L-DIN-C 153 101 50 20 4
2
5 4
2
3 r -2000S-DIN 131 79 50 20
a -2000S-DIN-C 131 79 50 20
20.0 3 r -2000L-DIN 153 101 50 20
5 a -2000L-DIN-C 153 101 50 20
5
RECOMMENDED CUTTING CONDITIONS
a MPS1 DRILL (3xD, 5xD)
Drill Diameter &3 &4 &5
Cutting Speed Cutting Speed
Work Material Conditions Cutting Speed Feed Feed Feed
(m/min) (mm/rev) (m/min) (mm/rev) (m/min) (mm/rev)
P Mild Steel Hardness
Carbon Steel
Alloy Steel < 180HB 100 (60150) 0.15 (0.10.2) 120 (70170) 0.19 (0.120.25) 130 (80190) 0.23 (0.150.3)
180 250HB 90 (60140) 0.15 (0.10.19) 100 (70160) 0.18 (0.120.24) 110 (80180) 0.22 (0.150.29)
280 350HB 80 (50110) 0.12 (0.10.14) 90 (60120) 0.15 (0.120.18) 90 (70140) 0.19 (0.150.22)
M Stainless Steel 40 (2050) 0.08 (0.060.12) 40 (3050) 0.09 (0.070.13) 40 (3050) 0.11 (0.080.16)
K Cast Iron < 350MPa 90 ( 60100) 0.15 (0.10.2)
< 450MPa 80 (5090) 100 (70110) 0.21 (0.120.3) 110 (80130) 0.25 (0.150.35)
Ductile Cast Iron < 800MPa 60 (4080) 0.12 (0.080.16)
0.09 (0.060.12) 90 (60100) 0.17 (0.10.24) 90 (70120) 0.21 (0.140.28)
70 (5090) 0.13 (0.080.18) 70 (60100) 0.17 (0.120.22)
Drill Diameter &6 &8 & 10
Cutting Speed
Work Material Conditions Cutting Speed Feed Feed Cutting Speed Feed DRILLING
(mm/rev) (m/min) (mm/rev) (m/min) (mm/rev)
Hardness (m/min)
P Mild Steel < 180HB 140 (90210) 0.27 (0.180.35) 160 (100240) 0.3 (0.20.4) 170 (100250) 0.33 (0.20.45)
Carbon Steel 180 250HB 120 (90190) 0.26 (0.180.33) 140 (100220) 0.29 (0.20.38) 150 (100230) 0.32 (0.20.43)
Alloy Steel 280 350HB 100 (80150) 0.22 (0.180.25)
120 (90170) 0.24 (0.20.27) 130 (90180) 0.25 (0.20.3)
M Stainless Steel 50 (4070) 0.14 (0.110.18) 50 (4070) 0.15 (0.120.2) 50 (4070) 0.16 (0.120.22)
K Cast Iron < 350MPa 120 (90140) 0.29 (0.180.4) 140 (100160) 0.33 (0.20.45) 150 (100170) 0.35 (0.20.5)
Ductile Cast Iron < 450MPa 100 (80130) 0.25 (0.160.34) 120 (90150) 0.28 (0.180.38) 130 (90160) 0.29 (0.180.4)
< 800MPa 80 (70110) 0.2 (0140.26)
100 (80130) 0.23 (0.160.3) 110 (80140) 0.24 (0.160.32)
Drill Diameter & 12 & 16 & 20
Conditions Cutting Speed
Work Material Feed Cutting Speed Feed Cutting Speed Feed
P Mild Steel Hardness (m/min) (mm/rev) (m/min) (mm/rev) (m/min) (mm/rev)
< 180HB 180 (100250) 0.35 (0.20.5) 180 (100250) 0.38 (0.20.55) 180 (100250) 0.4 (0.20.6)
Carbon Steel 180 250HB 160 (100230) 034 (0.20.48) 160 (100230) 0.36 (0.20.52) 160 (100230) 0.39 (0.20.57)
Alloy Steel 280 350HB 140 (90180) 0.27 (0.20.34)
140 (90180) 0.28 (0.20.36) 140 (90180) 0.3 (0.20.4)
M Stainless Steel 50 (4070) 0.18 (0.140.24) 50 (4070) 0.19 (0.150.26) 50 (4070) 0.21 (0.160.28)
K Cast Iron < 350MPa 160 (100170) 0.4 (0.20.6) 160 (100170) 0.43 (0.20..65) 160 (100170) 0.45 (0.20.7)
Ductile Cast Iron < 450MPa 140 (90160) 0.31 (0.180.44) 140 (90160) 0.33 (0.180.48) 140 (90160) 0.35 (0.180.52)
< 800MPa 110 (80140) 0.25 (0.160.34)
110 (80140) 0.27 (0.160.38) 110 (80140) 0.28 (0.160.4)
OPERATION GUIDANCE L034 L033
TECHNICAL DATA N001