RECOMMENDED CUTTING CONDITIONS
*y SHOULDER MILLING (At a small width of cut. )
Work Material Hardness Grade Cutting Speed Depth of Cut Cutting Width Feed per Tooth
vc ap ae fz
(m/min) (mm) (mm) (mm/tooth)
P Carbon Steel 180 280HB VP15TF 200 (80 300) < 0.05D1 < 0.05D1 0.2 ( < 0.4)
Alloy Steel
< 0.05D1
Pre-Hardened Steel < 45HRC VP15TF 150 (80 200) < 0.05D1 0.15 ( < 0.3)
Alloy Tool Steel 180 380HB VP15TF 150 (80 200) < 0.05D1 < 0.05D1 0.15 ( < 0.3)
M Stainless Steel 150 (100 200) < 0.05D1 < 0.05D1 0.2 ( < 0.4)
K Cast Iron < 270HB VP15TF 250 (180 450) < 0.05D1 < 0.05D1 0.3 ( < 0.4)
Tensile Strength MP8010 200 (80 300) < 0.05D1 < 0.1D1 0.3 ( < 0.4)
Ductile Cast Iron MP8010 100 (80 120) < 0.05D1 < 0.02D1 0.1 ( < 0.2)
H Hardened Steel < 350MPa MP8010
Tensile Strength
< 350MPa
45 55HRC
Hardened Steel 55 65HRC MP8010 80 (60 100) < 0.05D1 < 0.02D1 0.1 ( < 0.2)
* When the pick feed direction is along the axis of the tool such as finish machining at the wall part.
*y SLOTTING•SHOULDER MILLING (At a large width of cut. )
Work Material Hardness Grade Cutting Speed Depth of Cut Cutting Width Feed per Tooth
vc ap ae fz
(m/min) (mm) (mm) (mm/tooth)
P Carbon Steel 180 280HB VP15TF 200 (80 300) < 0.02D1 < D1 0.2 ( < 0.4)
Alloy Steel
Pre-Hardened Steel < 45HRC VP15TF 150 (80 200) < 0.02D1 < D1 0.15 ( < 0.3) ROTATING TOOLS
Alloy Tool Steel 180 380HB VP15TF 150 (80 200) < 0.02D1 < D1 0.15 ( < 0.3)
M Stainless Steel VP15TF 150 (100 200) < 0.02D1 < D1 0.2 ( < 0.4)
K Cast Iron < 270HB MP8010 250 (180 450) < 0.03D1 < D1 0.3 ( < 0.4)
Tensile Strength MP8010 200 (80 300) < 0.03D1 < D1 0.3 ( < 0.4)
Ductile Cast Iron MP8010 100 (80 120) < 0.01D1 < D1 0.1 ( < 0.2)
H Hardened Steel < 350MPa
Tensile Strength
< 350MPa
45 55HRC
Hardened Steel 55 65HRC MP8010 70 (60 80) < 0.01D1 < D1 0.1 ( < 0.2)
* When the feed is in the radial axis of the tool. E.g. machining a side wall.
(Note 1) Cutting conditions are for a standard steel shank type. If vibration or chipping of the insert occurs, reduce the cutting conditions
appropriately.
(Note 2) Cutting speed is calculated at the peripheral edge of the tool. Calculate spindle speed in the following way.
Spindle speed n(min-1)=1000Cutting speed vc uDiameter of cutting tool D1u3.14
(Note 3) Please note the following when machining hardened steel with MP8010.
• Shorten tool overhang as much as possible.
• Use a carbide shank type.
• Depth of cut setting is important to prevent fracture.